深圳市鹏科泰贸易有限公司

乐泰713促进剂

基本性能：

外观透明度/颜色：清澈

适用基材：氰基丙烯酸酯类胶粘剂，促进剂

 粘度：1

欲知更多产品详情，欢迎咨询深圳市鹏科泰贸易有限公司

网址：//pengketai.cn.alibaba.com/

电话：0755-86381816

传真：0755-86381822

以下价格仅供参考，具体价格面议！

PRODUCT DEscriptION
LOCTITE® Tak Pak® Accelerator 713 is a single-component,
medical grade, solvent-based accelerator for instant
adhesives. It is designed to speed the cure of Loctite
cyanoacrylate adhesives.

MEDICAL DEVICE BONDING
Cured product is certified for disposable medial device
applications. Loctite Tak Pak Accelerator 713 has been
tested by North American Science Associates (NAmSA) and
found to be in compliance with the requirements for USP
Class VI plastics. Tests included Acute Systemic Toxicity (T-
12), Intracutaneous Toxicity (T-13) and the Implantation Test
(T-14). Loctite Product 713 complies with the Loctite ISO-
10993 Biocompatibility test program. Certificates of
Compliance are available through the Loctite Quality
Department. Suitable for use in assembly of disposable
medical devices.
Approvals
Product 713 has been granted ISO-1099 which makes it
particularly suited for use in disposable medical device
assemblies.
Effects of Sterilization
In general, products similar in composition to Loctite Product
713 subjected to standard sterilization methods, such as EtO
and Gamma Radiation (25 to 50 kilorays cumulative) show
excellent bond strength retention. Product 713 maintains
bond strength after 1 cycle of steam autoclave. It is
recommended that customers test specific parts after
subjecting them to the preferred sterilization method. Consult
with Loctite for a product recommendation if your device will
see more than 3 sterilization cycles.
TYPICAL APPLICATIONS
· Printed circuit board wire tacking
· Tamperproofing of adjustable components
· Anywhere an instant surface cure of a cyanoacrylate
adhesive is desired.

PRODUCT FEATURES AND BENEFITS
· Speeds cure of Loctite cyanoacrylate adhesives
· Can be applied by spray, brush or drop
· Dries in seconds to speed assembly
· Improves cure through gap capability of Loctite
cyanoacrylates
LIQUID PROPERTIES
Typical Value
Chemical Type Organic amine
Appearance Clear amber liquid
Specific Gravity @ 25°C 0.8
Viscosity @ 68ºF, cP (20ºC, mPa.s) 1
Flash Point (TCC) 53ºF
Solvent Isopropanol
Drying time @ 68ºF/(20ºC),
seconds <30
On-part life, hours 1
Vapor pressure, mbar <50

PEFORMANCE
Fixture time and cure speed achieved by using Tak Pak
Accelerator 713 depend on the adhesive used and the
substrate bonded.
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected
with a sealant for chlorine or other strong oxidizing
materials.
For safe handling information on this product, consult
the Material Safety Data Sheet. (MSDS).
Where aqueous washing systems are used to clean the
surfaces before bonding, it is important to check for
compatibility of the washing solution with the activator and
adhesive. In some cases these aqueous washes can affect
the cure and performance of these materials. This product is
not normally recommended for use on plastics (particularly
thermoplastic materials where stress cracking of the plastic
could result). Users are recommended to /confirm/i
compatibility of the product with such substrates.
USE AND APPLICATION
An accelerator is a substance that speeds a reaction. This
product can be applied after the application of a Loctite
cyanoacrylate adhesive to speed up cure.
Post-Acceleration
1. Apply Loctite cyanoacrylate to the parts to be bonded or
fixed.
2. Apply accelerator over adhesive by spray or by drop.
Use one drop of accelerator per one drop of adhesive.

HANDLING PRECAUTIONS
Under no circumstances should the accelerator and adhesive
be directly mixed as liquids.
The carrying solvent can affect certain plastics or coatings. It
is recommended that all surfaces be tested for compatibility
before use.
Storage
Product shall be ideally stored in a cool, dry location in
unopened containers at a temperature between 8°C to 28°C
(46°F to 82°F) unless otherwise labeled. Optimal storage is
at the lower half of this temperature range.